QB/T 2665-2004 Polyethylene terephthalate (PET) bottles for hot filling
Some standard content:
Ics83.can
Classification number: G33
Registration number: 15130-2005
Light Industry Standard of the People's Republic of China
QB/T2665—2004
Hot filling polyethylene terephthalate (PET) bottleHeat resistant polyethylene terephthalate (rET) bottle2004-12-14 Issued
National Development and Reform Commission of the People's Republic of China Implemented on 2005-06-01
QB/T26652004
Please note that the contents of this standard may have patents. The issuing organization of this standard shall not intend to identify these patents. Appendix A of this standard is an informative appendix.
The standard is proposed by China Light Industry Federation. This standard is issued by the National Plastic Products Standardization Technical Committee. This standard is from Zhongchan Industrial Co., Ltd. The drafters of the standard are Huang Leda, Lu Fangcheng, Huang Chaohu, Xu Zheng, and Ben Yidu. The Shenzhen Standard is first published.
YKANYKea=
1Fanyuan
Polyethylene terephthalate (PET) bottle for hot filling QB/T2665-2C04
Does not include the definition, product classification, requirements, safety regulations, qualification rules, packaging, confirmation, and some existence of poly(ethylene terephthalate) board. This standard uses polyol as the main raw material, and is used for making plastic bottles for filling agents through filament, drawing and blow molding.
2 Normative referenced documents
The following clauses are generally accepted by the general public and become the clauses of this standard. All the documents of the production plan, all subsequent orders (excluding the rate of error) or revisions or uniformity are applicable to this standard. However, the parties concerned may study and use these documents as new versions based on the agreement reached on this standard: For any outdated documents, their latest versions shall apply to this standard GB/2828.1-2003 Sample inspection procedure Part 1: Batch sample plan for acceptance pressure (AQL) inspection GB/T291B-1998 Plastic test standard GR13? Food containers and packaging materials standard QB/1868-2004 Polyethylene glycol, PET> Ethylene glycol beverage bottle 3 Definitions
The following are applicable standards! 3.2
Nominal wear
After hot loading, the volume of the material after cooling for 20 seconds, 3.3
Verticality
Deviation between the center line of the bottom half and the vertical axis. 3.4
Vacuum degree|| tt||The ability to resist the deterioration of the body caused by the internal negative pressure after heat treatment: 4 Product classification
4.1 The color of the bottle is the colored bottle 4.2 The product is divided into the colored bottle and the non-crystal bottle according to the demand. 4.3 According to the shape, it is divided into round and square bottles, etc. 5 Requirements
5.1 Appearance
Complete specification
QB/T2665··2004
5.2 Specifications and deviations
5.21 Height deviation
Should meet the requirements of Table 2,
Table "Appearance Requirements
Should meet the requirements of Table 2, ... -- 95
Minimum wall thickness of each part shall be in accordance with the table 4 Minimum penetration thickness
Verticality
The deviation of the center line of the component to the plane of the store shall be determined by the combination of 5, Table 5 Verticality Body Bacteria
High Beijing Institute
HYKANYKa
According to the limit difference
The minimum limit
Annual recovery*
Unit is three meters
Single main is safety technology
5.2.5 The capacity of the national code
shall comply with the provisions of this 6.
F01--125u
: 251- -2 0[)
5 3 Physical and mechanical properties
Institute of mechanical properties and its derivatives in Table 7:
Vertical height/N
Cargo load
Shape system space/rmil
Table B Capacity deviation
Full 1 person (85 pieces
Visual flow car
Parts energy (2m)
Average deviation
Table of physical and mechanical properties
: 500 m:L ih
2nanil.游
Note: Other display time and true middle requirements are determined by the supply and demand, 5. 4 Heat resistance
Should comply with the provisions of Table 8:
Q8/T2865.--2994
Nominal wear maximum (20C)
Ji Yang stop
: Icki
New body acid cracking
OB/T2665-2004
Volume recovery rate/%
Confirm shrinkage change%
In addition, the length shrinkage single statement can be signed or described:
Apply for length change recovery average
Part mutual method rate
5.5 Acetaldehyde content
Degree is in line with the regulations of today's journal 9
Natural content
Health index
Seat meets the requirements of 13113:
Test method
Sample state adjustment and test standard environment Table 8 Heat resistance
300 mL-- 1 25U mL
:251mL--2000ml
Bottle wear has no obvious shrinkage deformation, no convexity. Table 9 Acetyl Content
No fish oil:
Controlled according to the standard environment and tolerance range specified in B/2918-1998. 6.2 Appearance
Measured under natural light or lamp.
63 Specifications
6.3.1 Requirements for measuring annual bottles with a height difference of 0.mm:
6.3.2 Diameter or side length deviation
Use a ring with a diameter of .02mm and a measuring plate, 5.3.3 Minimum wall thickness
Use a ring with a diameter of .02mm and a measuring plate, 5.3.3 Minimum wall thickness
Use a ring with a diameter of .02mm and a measuring plate, 5.3.3 Minimum wall thickness
Use a ring with a diameter of .02mm and a measuring plate, 5.3.4 ... Y KNr Ka=
6.3.5 Capacity increase deviation
White.3.5.1 Capacity calculation formula
Yan wear volume calculation formula (1)
Where:
P--capacity of the bottle, in liters (mT.): total mass of the bottle, in grams (g)
Mass of the empty bottle: in grams ():
: surface density of the water separated from the steam, in grams (m!) Calculate the deviation of the bottle capacity by formula (2).
Bottle capacity limit deviation: in liters (
--actual capacity of the bottle, in liters (mI,): nominal density, millimeters (.
6.3.5.2 Full capacity deviation
QB/T 2665-2004
The empty moment quality, the basis to .1, quickly retreat the teeth (85+1) water to the mouth, that is, you to the root and the water inside the basis, according to formula! 1 will be the water quality according to the water suitable for storage into full! Customer volume. According to formula 2) calculate the full customer early limit deviation, full capacity: average deviation card then receive various full capacity [capacity basic limit deviation arithmetic mean. 6.3.5.3 Consult the volume required
weigh the quality letter, the village confirmed to 0.1, the rapid filling (851) water year to obtain the community point, immediately weigh the bottle and the water quality, according to formula (1) the quality of the reference to receive 20 water The actual wear is converted into nominal wear: Formula (2) Calculate the nominal wear limit difference, the nominal wear limit difference measurement limit and the nominal wear limit difference measurement limit are calculated, 6.4 Mechanical properties
6.4.1 Vertical load pressure
6.4.1.1 Vertical load pressure of empty bottles
Select 10 samples, (232) place them for 2h, place them on the test machine, and press the bottles at a constant speed of 100mm/m until they feel the force, record the initial load, and calculate the arithmetic mean of the results. 6.4.1.2 Preparation of water sample bottles
Take 2 bottles, fill them with (51) water to the injection point and then seal them. Use water cooling belt 6.4.1.3 to make them full and then vertically load them.
Take 10 bottles filled with water according to method 0.4.1.2, (23 ± 2) and place them for more than 2 hours. Each bottle is placed on the pressure test machine. The initial maximum load is recorded, accurate to 1N, and the arithmetic mean of the load is calculated. 4.2 Bottle wall load
6.4.2.1 Bottle wall plate negative exposure
connection h.4.1. 2. Take 10 bottles of water samples and place them on the pressure test machine (Figure 1) at 23+2 for more than 2h. Apply pressure to the sample plates at a constant speed of 50mm/m. Record the maximum load to the nearest 1:1. Calculate the arithmetic average of the measurement results.
(B/T2665-2CC4
8.4.2.2 Longitudinal load
04.1.2 Take 10 bottles of water samples and place them on the pressure test machine (Figure 2) at 23+2 for more than 2h. Apply pressure to the sample plates at a constant speed of 50mm/m. Record the maximum load to the nearest 1:1. Calculate the arithmetic average of the measurement results to the nearest 1:1. Calculate the arithmetic average of the measurement results to the nearest 1:1. 3 Vacuum resistance
Figure 2 Schematic diagram of damageable strength load
10 bottles, divided into blue and dirty room temperature water, use a rubber diaphragm, insert a needle into the bottle, the line is extended to the level (1 unit), press the meter, measure the volume of water in the bottle, take a sample of the test results and average the results. 6.4.4 Drop performance
6.41.1.2 Method Table Collect 10 water-containing sample bottles and determine them according to 6.6.3 of OB/186R-2004. 6.5 Heat resistance
6.5.1 Volume shrinkage
10 bottles, divided into blue and dirty room temperature water, use a rubber diaphragm, insert a needle into the bottle, the line is extended to the level (1 unit), press the meter, measure the volume of water in the bottle, take a sample of the test results and average the results. 6.4.4 Drop performance
6.41.1.2 Method Table Collect 10 water-containing sample bottles and determine them according to 6.6.3 of OB/186R-2004. 6.5 Heat resistance
6.5.1 Volume shrinkage
10 bottles, divided into blue and dirty room temperature water, weigh the water quality of the empty bottles, Accurate to 0.1, then calculate the full mouth volume before filling with hot water: Formula 1 and the end of the hot water filling volume, water drain, swim full (85 three 1) core heat, cover, cool with water to normal benefit, and then calculate the room temperature separately, weigh the empty bottle and water quality before: Accurate to 1: Two separate calculations, Formula 1) Calculate the full mouth volume after filling with hot water: Formula () Calculate the optimal shrinkage rate, Han plan presents the result point person estimate X,
volume recovery rate, 5:
Ekx100
The full mouth volume before filling with hot water is checked, the unit is liter (ml.): The full mouth volume after hot water filling is checked, the unit is liter (called
6.5.2 High check collection wear, diameter or side length shrinkage: 31
Take 10 A bottle, connected to 6 3.2 and 6.3.3 period of height and straight or long film, evil into (95 +:) T heat not to the injection point, blue, water placed 30:, stand 205, and ask the cooling rate in the over, the case is a sign of music, the board body has a shrinkage, reduce the height and diameter or length, respectively, the formula (4, formula () to calculate the height shrinkage rate, diameter or length shrinkage rate, then the maximum value. G
HIYKAoNY Ka=
In the formula:
Wu Zhong:
Height no shrinkage rate, head:
H-HLi×100
This is the total height of the bottle before the hot water injection, the unit is meter (mm) and the hot water injection block, the unit is the relative (mm). .
Hundred diameter shrinkage rate, must be:
. — Diameter of sample bottle before unpainting, unit price is meter (m) — Diameter of sample bottle after painting, total constant is millimeter (mn) 6.6 Acetaldehyde content
According to 6.8 of QB/186-2004. 6! Hygiene index
GH13113 is carried out according to
7 Inspection rules
QB/T2665-2004
7.1 Batch
products are inspected as units, with the same number, the same specification of materials, the same process of production of the return of investment products, each batch should not exceed 100,000, not more than 100 square meters, and the number of products produced more than 3 days is a batch. 72 Sampling
external certification, period and pollution adopt G/T2828. 1-2003% machine price, normal-time sampling, special inspection level S-4AQ, 4.0. Table 10 stipulates. Heat-resistant pen, secret physical properties are based on the table, randomly deduct 80 samples from each industry for inspection: Table 10 sample set
91--150
151~-260
251--:00
501-1200
1201:-3200
1291 ~110
1n(13(
35 201-[50 360
155160
These are individual
certificates
QB/T2665—2004
1.3 Factory inspection
! The inspection items are 5.1, 5.2.2, 5.3. Particularly the product ratios in Table 8 7.4 Type inspection
When any of the following conditions is met, type inspection shall be carried out: 7.4.1
Trial design for production or conversion of old products:
After production , materials, "art bamboo shoots teach people to change the product energy time: 6)
product suspension for more than three months, the original time of the production change:
) stop production, pay at least once a year for type inspection, 7.4.2 special inspection of the oil in the mountain, all the awards, 75 qualified batches of judgment
external notes, specifications and deviations are shown in Table 1. Thermal properties and mechanical properties of the material are tested, if one item is unqualified, the original batch will be deducted from the effective sample The product re-inspection failed the item, and the inspection result was: the whole batch was qualified. Chemical and sanitary indicators were inspected, among which the typical failed, and the whole batch was unqualified.
day marking, packaging, transportation, storage
day. 1.1 There should be special recycling marks on the product body. 8.1.2 The product should have the following marks on the chain: individual labels: product name, appearance, reduction list, quantity, net weight, packaging, production, production, cooling, address, transportation and storage, etc. 8.2 Packaging The packaging should be able to ensure that the product will not be damaged or contaminated by other substances during transportation and storage. 8.3 During transportation, the product should be clean and disinfected, and prevented from being pressed and placed properly. 8.4 The product should be stored in a dry, dry and chemical-free warehouse without harmful substances. The product should be stored in a well-maintained place for 15 days to reduce the heat before transportation. The product can be tested and can not exceed 3 days from the date of production. HY KANY Ka
Appendix A
: Properties of porcelain materials
Table of water in air Nanliang Table
C P9B8T
t: uux 21
G44x41
0. 998 45
i. yu gri
.yuh *s
QB/T2665-2004
wg·ml:
0. 995 77
0. 995 51
0. 995 25
0. 9-13 39
u. 99.: 05
0. 992 71
0. 992.35
0. 991 63
099387
QR:T 2665-2004
/()
0. 980 21
6. 979 13
( 76 33 | | tt | 82
699967
1 9554723+2) Place the bottle on the pressure test machine (Figure 1) for more than 2h, and apply pressure to the sample plate at a constant speed of 50mm/m, record the maximum load, and calculate the arithmetic average of the measurement results.
(B/T2665-2CC4
8.4.2.2 Longitudinal reinforcement load
04.1.2 Take 10 water-carrying bottles respectively, and place them on the pressure test machine (Figure 2) at (23+20, and 21+3), and apply pressure to the bottles in the same direction at a constant speed of 511mm/min, and record the maximum load to the nearest N. Calculate the arithmetic average of the measurement results: 2
Figure 1 Schematic diagram of bottle wall plate load
6. 4. 3 Vacuum resistance
Figure 2 Schematic diagram of damageable strength load
10 bottles, divided into blue and dirty room temperature water, use a rubber diaphragm, insert a needle into the bottle, the line is extended to the level (1 unit), press the meter, measure the volume of water in the bottle, take a sample of the test results and average the results. 6.4.4 Drop performance
6.41.1.2 Method Table Collect 10 water-containing sample bottles and determine them according to 6.6.3 of OB/186R-2004. 6.5 Heat resistance
6.5.1 Volume shrinkage
10 bottles, divided into blue and dirty room temperature water, use a rubber diaphragm, insert a needle into the bottle, the line is extended to the level (1 unit), press the meter, measure the volume of water in the bottle, take a sample of the test results and average the results. 6.4.4 Drop performance
6.41.1.2 Method Table Collect 10 water-containing sample bottles and determine them according to 6.6.3 of OB/186R-2004. 6.5 Heat resistance
6.5.1 Volume shrinkage
10 bottles, divided into blue and dirty room temperature water, weigh the water quality of the empty bottles, Accurate to 0.1, then calculate the full mouth volume before filling with hot water: Formula 1 and the end of the hot water filling volume, water drain, swim full (85 three 1) core heat, cover, cool with water to normal benefit, and then calculate the room temperature separately, weigh the empty bottle and water quality before: Accurate to 1: Two separate calculations, Formula 1) Calculate the full mouth volume after filling with hot water: Formula () Calculate the optimal shrinkage rate, Han plan presents the result point person estimate X,
volume recovery rate, 5:
Ekx100
The full mouth volume before filling with hot water is checked, the unit is liter (ml.): The full mouth volume after hot water filling is checked, the unit is liter (called
6.5.2 High check collection wear, diameter or side length shrinkage: 31
Take 10 A bottle, connected to 6 3.2 and 6.3.3 period height and straight or long film, evil into (95 +:) T heat not to the point, blue, water placed 30:, stand 205, and ask the cooling rate in the over, the case is a sign of music, the board body has a shrinkage color, reduce the height and diameter or step length, respectively, the effective formula (4, formula () to calculate the height shrinkage rate, branch diameter or length shrinkage rate, then the maximum value is obtained. G
HIYKAoNY Ka=
Where:
Height shrinkage rate, head:
H-HLi×100Www.bzxZ.net
Height of the bottle before hot water injection, unit is meter (mm) Height of the hot water injection, unit is mm. .
Diameter shrinkage rate, must be:
. —Diameter of the sample bottle before hot water injection, unit is meter (m) —Diameter of the sample bottle after hot water injection, total is mm (mn) 6.6 Acetaldehyde content
Measured according to 6.8 in QB/186-2004. 6! Hygiene index
GH13113 for standard inspection
7 Inspection rules
QB/T2665-2004
7.1 Batch
products are inspected as units, with the same number, specifications of materials, and the same process of production of "return products", each batch should not exceed 100,000 pieces, and no more than 100 pieces produced in more than 3 days as a batch. 72 sampling
external certification, period and pollution measures shall adopt G/T2828. 1-2003% machine price, normal-time sampling, special inspection level S-4AQ, 4.0. Table 10 stipulates. Heat-resistant pen, secret physical properties are based on the table, randomly deduct 80 samples from each industry for inspection: Table 10 sample set
91--150
151~-260
251--:00
501-1200
1201:-3200
1291 ~110
1n(13(
35 201-[50 360
155160
These are individual
certificates
QB/T2665—2004
1.3 Factory inspection
! The inspection items are 5.1, 5.2.2, 5.3. Particularly the product ratios in Table 8 7.4 Type inspection
When any of the following conditions is met, type inspection shall be carried out: 7.4.1
Trial design for production or conversion of old products:
After production , materials, "art bamboo shoots teach people to change the product energy time: 6)
product suspension for more than three months, the original time of the production change:
) stop production, pay at least once a year for type inspection, 7.4.2 special inspection of the oil in the mountain, all the awards, 75 qualified batches of judgment
external notes, specifications and deviations are shown in Table 1. Thermal properties and mechanical properties of the material are tested, if one item is unqualified, the original batch will be deducted from the effective sample The product re-inspection failed the item, and the inspection result was: the whole batch was qualified. Chemical and sanitary indicators were inspected, among which the typical failed, and the whole batch was unqualified.
day marking, packaging, transportation, storage
day. 1.1 There should be special recycling marks on the product body. 8.1.2 The product should have the following marks on the chain: individual labels: product name, appearance, reduction list, quantity, net weight, packaging, production, production, cooling, address, transportation and storage, etc. 8.2 Packaging The packaging should be able to ensure that the product will not be damaged or contaminated by other substances during transportation and storage. 8.3 During transportation, the product should be clean and disinfected, and prevented from being pressed and placed properly. 8.4 The product should be stored in a dry, dry and chemical-free warehouse without harmful substances. The product should be stored in a well-maintained place for 15 days to reduce the heat before transportation. The product can be tested and can not exceed 3 days from the date of production. HY KANY Ka
Appendix A
: Properties of porcelain materials
Table of water in air Nanliang Table
C P9B8T
t: uux 21
G44x41
0. 998 45
i. yu gri
.yuh *s
QB/T2665-2004
wg·ml:
0. 995 77
0. 995 51
0. 995 25
0. 9-13 39
u. 99.: 05
0. 992 71
0. 992.35
0. 991 63
099387
QR:T 2665-2004
/()
0. 980 21
6. 979 13
( 76 33 | | tt | 82
699967
1 9554723+2) Place the bottle on the pressure test machine (Figure 1) for more than 2h, and apply pressure to the sample plate at a constant speed of 50mm/m, record the maximum load, and calculate the arithmetic average of the measurement results.
(B/T2665-2CC4
8.4.2.2 Longitudinal reinforcement load
04.1.2 Take 10 water-carrying bottles respectively, and place them on the pressure test machine (Figure 2) at (23+20, and 21+3), and apply pressure to the bottles in the same direction at a constant speed of 511mm/min, and record the maximum load to the nearest N. Calculate the arithmetic average of the measurement results: 2
Figure 1 Schematic diagram of bottle wall plate load
6. 4. 3 Vacuum resistance
Figure 2 Schematic diagram of damageable strength load
10 bottles, divided into blue and dirty room temperature water, use a rubber diaphragm, insert a needle into the bottle, the line is extended to the level (1 unit), press the meter, measure the volume of water in the bottle, take a sample of the test results and average the results. 6.4.4 Drop performance
6.41.1.2 Method Table Collect 10 water-containing sample bottles and determine them according to 6.6.3 of OB/186R-2004. 6.5 Heat resistance
6.5.1 Volume shrinkage
10 bottles, divided into blue and dirty room temperature water, use a rubber diaphragm, insert a needle into the bottle, the line is extended to the level (1 unit), press the meter, measure the volume of water in the bottle, take a sample of the test results and average the results. 6.4.4 Drop performance
6.41.1.2 Method Table Collect 10 water-containing sample bottles and determine them according to 6.6.3 of OB/186R-2004. 6.5 Heat resistance
6.5.1 Volume shrinkage
10 bottles, divided into blue and dirty room temperature water, weigh the water quality of the empty bottles, Accurate to 0.1, then calculate the full mouth volume before filling with hot water: Formula 1 and the end of the hot water filling volume, water drain, swim full (85 three 1) core heat, cover, cool with water to normal benefit, and then calculate the room temperature separately, weigh the empty bottle and water quality before: Accurate to 1: Two separate calculations, Formula 1) Calculate the full mouth volume after filling with hot water: Formula () Calculate the optimal shrinkage rate, Han plan presents the result point person estimate X,
volume recovery rate, 5:
Ekx100
The full mouth volume before filling with hot water is checked, the unit is liter (ml.): The full mouth volume after hot water filling is checked, the unit is liter (called
6.5.2 High check collection wear, diameter or side length shrinkage: 31
Take 10 A bottle, connected to 6 3.2 and 6.3.3 period height and straight or long film, evil into (95 +:) T heat not to the point, blue, water placed 30:, stand 205, and ask the cooling rate in the over, the case is a sign of music, the board body has a shrinkage color, reduce the height and diameter or step length, respectively, the effective formula (4, formula () to calculate the height shrinkage rate, branch diameter or length shrinkage rate, then the maximum value is obtained. G
HIYKAoNY Ka=
Where:
Height shrinkage rate, head:
H-HLi×100
Height of the bottle before hot water injection, unit is meter (mm) Height of the hot water injection, unit is mm. .
Diameter shrinkage rate, must be:
. —Diameter of the sample bottle before hot water injection, unit is meter (m) —Diameter of the sample bottle after hot water injection, total is mm (mn) 6.6 Acetaldehyde content
Measured according to 6.8 in QB/186-2004. 6! Hygiene index
GH13113 for standard inspection
7 Inspection rules
QB/T2665-2004
7.1 Batch
products are inspected as units, with the same number, specifications of materials, and the same process of production of "return products", each batch should not exceed 100,000 pieces, and no more than 100 pieces produced in more than 3 days as a batch. 72 sampling
external certification, period and pollution measures shall adopt G/T2828. 1-2003% machine price, normal-time sampling, special inspection level S-4AQ, 4.0. Table 10 stipulates. Heat-resistant pen, secret physical properties are based on the table, randomly deduct 80 samples from each industry for inspection: Table 10 sample set
91--150
151~-260
251--:00
501-1200
1201:-3200
1291 ~110
1n(13(
35 201-[50 360
155160
These are individual
certificates
QB/T2665—2004
1.3 Factory inspection
! The inspection items are 5.1, 5.2.2, 5.3. Particularly the product ratios in Table 8 7.4 Type inspection
When any of the following conditions is met, type inspection shall be carried out: 7.4.1
Trial design for production or conversion of old products:
After production , materials, "art bamboo shoots teach people to change the product energy time: 6)
product suspension for more than three months, the original time of the production change:
) stop production, pay at least once a year for type inspection, 7.4.2 special inspection of the oil in the mountain, all the awards, 75 qualified batches of judgment
external notes, specifications and deviations are shown in Table 1. Thermal properties and mechanical properties of the material are tested, if one item is unqualified, the original batch will be deducted from the effective sample The product re-inspection failed the item, and the inspection result was: the whole batch was qualified. Chemical and sanitary indicators were inspected, among which the typical failed, and the whole batch was unqualified.
day marking, packaging, transportation, storage
day. 1.1 There should be special recycling marks on the product body. 8.1.2 The product should have the following marks on the chain: individual labels: product name, appearance, reduction list, quantity, net weight, packaging, production, production, cooling, address, transportation and storage, etc. 8.2 Packaging The packaging should be able to ensure that the product will not be damaged or contaminated by other substances during transportation and storage. 8.3 During transportation, the product should be clean and disinfected, and prevented from being pressed and placed properly. 8.4 The product should be stored in a dry, dry and chemical-free warehouse without harmful substances. The product should be stored in a well-maintained place for 15 days to reduce the heat before transportation. The product can be tested and can not exceed 3 days from the date of production. HY KANY Ka
Appendix A
: Properties of porcelain materials
Table of water in air Nanliang Table
C P9B8T
t: uux 21
G44x41
0. 998 45
i. yu gri
.yuh *s
QB/T2665-2004
wg·ml:
0. 995 77
0. 995 51
0. 995 25
0. 9-13 39
u. 99.: 05
0. 992 71
0. 992.35
0. 991 63
099387
QR:T 2665-2004
/()
0. 980 21
6. 979 13
( 76 33 | | tt | 82
699967
1 955471, then the original sea: the nuclear formula 1 calculation and the end of the hot water before the full mouth volume, water drainage, swim full (85 three 1) hot, cover, cool with water to normal benefit, and then respectively at room temperature, weigh the empty bottle and water quality before: fine Xie to 1: two separately calculate the wet, formula 1) to calculate the full mouth volume after filling with hot water: formula () calculate the optimal shrinkage rate, the Han plan presents the result of the estimated point X,
volume recovery rate, 5:
Ekx100
end of the hot water before the full mouth volume check, the unit is liter (ml.): hot small after the full wear product, the unit is liter (called
6.5.2 high check wear, diameter or side length shrinkage: 31
take 10 dead bottles, connect 6 3.2 and 6.3.3 period height and straight or long slice, evil into (95+:) T heat has not reached the point of attention, the water has been placed for 30:, stand 205, and ask for the cooling rate in the over, the case is a sign of music, the board body has a shrinkage color, reduce the height and diameter or length, respectively, the effective formula (4, formula () to calculate the height shrinkage rate, the diameter or length shrinkage rate, then the maximum value is obtained. G
HIYKAoNY Ka=
Where:
Height shrinkage rate, head:
H-HLi×100
Height of the bottle before hot water injection, unit is meter (mm) Height of the hot water injection, unit is mm. .
Diameter shrinkage rate, must be:
. —Diameter of the sample bottle before hot water injection, unit is meter (m) —Diameter of the sample bottle after hot water injection, total is mm (mn) 6.6 Acetaldehyde content
Measured according to 6.8 of QB/186-2004. 6! Hygiene index
GH13113 for you
7 Inspection rules
QB/T2665-2004
7.1 Batch||tt| |The products are inspected and accepted by the unit, and the "returned products" produced by the same number, specification, and process are used. Each batch should not exceed 100,000 pieces, and no more than 100 pieces are produced in more than 3 days. 72 sampling
external certificate, period and pollution adopt G/T2828.1-2003% machine pricing, normal-second sampling, special inspection level S-4AQ, 4.0. Table 10 stipulates. Heat-resistant pen, secret physical properties are shown in the table, and 80 pieces are randomly deducted from each unit for inspection: Table 10 sample set
91--150
151~-260
251--:00
501-1200
1201:-3200
1291 ~110
1n(13(
35 201-[50 360
155160
These are individual
certificates
QB/T2665—2004
1.3 Factory inspection
! The inspection items are 5.1, 5.2.2, 5.3. The product ratios in Table 8 are shown in Table 8. 7.4 Type inspection
When any of the following conditions is met, type inspection shall be carried out: 7.4.1
Replacement of old products or conversion of old products 6)
Product suspension for more than three months, production change:
)Product suspension for a longer period of time, at least one type inspection shall be carried out each year, 7.4.2 Special inspection: All the qualified batches shall be determined according to the specifications and deviations shown in Table 1. Thermal properties and mechanical properties inspection: If one item is unqualified, a sample of twice the original batch shall be deducted for re-inspection of the unqualified item, and the inspection result: the whole batch is qualified. Chemical and sanitary indexes are tested at the inspection station. Among them, the whole batch is unqualified and the marking, packaging, transportation, storage and recycling are unqualified. 1.1 The product should have special marks on the body of the piece. 8.1.2 The products should have the following marks on the legal chain: individual marks: product weight, appearance, reduction, quantity, net weight, packaging, production, production, cooling, individual weight, product number, production process, etc. Pay attention to the inspection address, transportation and storage of the product. 8.2 Packaging The packaging label should be able to ensure that the products will not be damaged or contaminated by related objects during transportation and storage of the enterprise. 8.3 Transportation
Products should be clean and disinfected, and should be protected from pressure and pressure. 8.4 Product storage
Products should be stored in a well-ventilated, dry place without chemicals and harmful substances. The product should be stored for 15 days to reduce the heat before transportation. The product can only be stored after testing. The storage period should not exceed 3 days from the date of production. HY KANY Ka
Appendix A
: Properties of porcelain materials
Table of water in air
C P9B8T
t: uux 21
G44x41
0. 998 45
i. yu gri
.yuh *s
QB/T2665-2004
wg·ml:
0. 995 77
0. 995 51
0. 995 25
0. 9-13 39
u. 99.: 05
0. 76 33 | | tt | 82
699967
1 955471, then the original sea: the nuclear formula 1 calculation and the end of the hot water before the full mouth volume, water drainage, swim full (85 three 1) hot, cover, cool with water to normal benefit, and then respectively at room temperature, weigh the empty bottle and water quality before: fine Xie to 1: two separately calculate the wet, formula 1) to calculate the full mouth volume after filling with hot water: formula () calculate the optimal shrinkage rate, the Han plan presents the result of the estimated point X,
volume recovery rate, 5:
Ekx100
end of the hot water before the full mouth volume check, the unit is liter (ml.): hot small after the full wear product, the unit is liter (called
6.5.2 high check wear, diameter or side length shrinkage: 31
take 10 dead bottles, connect 6 3.2 and 6.3.3 period height and straight or long slice, evil into (95+:) T heat has not reached the point of attention, the water has been placed for 30:, stand 205, and ask for the cooling rate in the over, the case is a sign of music, the board body has a shrinkage color, reduce the height and diameter or length, respectively, the effective formula (4, formula () to calculate the height shrinkage rate, the diameter or length shrinkage rate, then the maximum value is obtained. G
HIYKAoNY Ka=
Where:
Height shrinkage rate, head:
H-HLi×100
Height of the bottle before hot water injection, unit is meter (mm) Height of the hot water injection, unit is mm. .
Diameter shrinkage rate, must be:
. —Diameter of the sample bottle before hot water injection, unit is meter (m) —Diameter of the sample bottle after hot water injection, total is mm (mn) 6.6 Acetaldehyde content
Measured according to 6.8 of QB/186-2004. 6! Hygiene index
GH13113 for you
7 Inspection rules
QB/T2665-2004
7.1 Batch||tt| |The products are inspected and accepted by the unit, and the "returned products" produced by the same number, specification, and process are used. Each batch should not exceed 100,000 pieces, and no more than 100 pieces are produced in more than 3 days. 72 sampling
external certificate, period and pollution adopt G/T2828.1-2003% machine pricing, normal-second sampling, special inspection level S-4AQ, 4.0. Table 10 stipulates. Heat-resistant pen, secret physical properties are shown in the table, and 80 pieces are randomly deducted from each unit for inspection: Table 10 sample set
91--150
151~-260
251--:00
501-1200
1201:-3200
1291 ~110
1n(13(
35 201-[50 360
155160
These are individual
certificates
QB/T2665—2004
1.3 Factory inspection
! The inspection items are 5.1, 5.2.2, 5.3. The product ratios in Table 8 are shown in Table 8. 7.4 Type inspection
When any of the following conditions is met, type inspection shall be carried out: 7.4.1
Replacement of old products or conversion of old products 6)
Product suspension for more than three months, production change:
)Product suspension for a longer period of time, at least one type inspection shall be carried out each year, 7.4.2 Special inspection: All the qualified batches shall be determined according to the specifications and deviations shown in Table 1. Thermal properties and mechanical properties inspection: If one item is unqualified, a sample of twice the original batch shall be deducted for re-inspection of the unqualified item, and the inspection result: the whole batch is qualified. Chemical and sanitary indexes are tested at the inspection station. Among them, the whole batch is unqualified and the marking, packaging, transportation, storage and recycling are unqualified. 1.1 The product should have special marks on the body of the piece. 8.1.2 The products should have the following marks on the legal chain: individual marks: product weight, appearance, reduction, quantity, net weight, packaging, production, production, cooling, individual weight, product number, production process, etc. Pay attention to the inspection address, transportation and storage of the product. 8.2 Packaging The packaging label should be able to ensure that the products will not be damaged or contaminated by related objects during transportation and storage of the enterprise. 8.3 Transportation
Products should be clean and disinfected, and should be protected from pressure and pressure. 8.4 Product storage
Products should be stored in a well-ventilated, dry place without chemicals and harmful substances. The product should be stored for 15 days to reduce the heat before transportation. The product can only be stored after testing. The storage period should not exceed 3 days from the date of production. HY KANY Ka
Appendix A
: Properties of porcelain materials
Table of water in air
C P9B8T
t: uux 21
G44x41
0. 998 45
i. yu gri
.yuh *s
QB/T2665-2004
wg·ml:
0. 995 77
0. 995 51
0. 995 25
0. 9-13 39
u. 99.: 05
0. 76 33 | | tt | 82
699967
1 955477.4 Type inspection
When any of the following conditions are met, type inspection shall be carried out: 7.4.1
Trial production or conversion of old products:
After production is stopped, materials, "artificial bamboo shoots teach people to change the product performance: 6)
Production is stopped for more than three months, and the production is changed:
)When production is stopped, type inspection shall be carried out at least once a year. 7.4.2 Type inspection All the standard oils in this product shall be judged according to the award pieces, and the specifications and deviations shall be shown in Table 1. When the thermal performance and mechanical properties are tested, if one of the items is unqualified, the effective sample of the original batch shall be deducted for re-testing the unqualified items. The test results are as follows: the whole batch is qualified. Chemical and sanitary indexes are tested, and if the typical items are unqualified, the whole batch is unqualified. t||日 Marking, packaging, transportation, storage
日.1.1 The product should have special recycling labels on the body. 8.1.2 The product should have the following labels on the legal chain: individual labels: product weight, quantity, net weight, packaging, production, production, name & address, transportation and storage, etc. 8.2 Packaging
The packaging label should be able to ensure the safety of the product during transportation in the enterprise 8.3 During transportation, the products shall be clean, disinfected, and prevented from being pressed and placed properly. 8.4 Products shall be stored in a dry, clean, and dry place without any chemicals or harmful substances. The products shall be stored in a well-maintained place for 15 days to reduce the heat before transportation. The products shall not be stored for more than 3 days from the date of production. KANY Ka
Appendix A
: Record of Porcelain Properties
Table of Water in Air Nanliang Table
C P9B8T
t: uux 21
G44x41
0. 998 45
i. yu gri
.yuh *s
QB/T2665-2004
wg·ml:
0. 995 77
0. 995 51
0. 995 25
0. 9-13 39
u. 99.: 05
0. 992 71
0. 992.35
0. 991 63
099387
QR:T 2665-2004
/()
0. 980 21
6. 979 13
( 76 33 | | tt | 82
699967
1 955477.4 Type inspection
When any of the following conditions are met, type inspection shall be carried out: 7.4.1
Trial production or conversion of old products:
After production is stopped, materials, "artificial bamboo shoots teach people to change the product performance: 6)
Production is stopped for more than three months, and the production is changed:
)When production is stopped, type inspection shall be carried out at least once a year. 7.4.2 Type inspection All the standard oils in this product shall be judged according to the award pieces, and the specifications and deviations shall be shown in Table 1. When the thermal performance and mechanical properties are tested, if one of the items is unqualified, the effective sample of the original batch shall be deducted for re-testing the unqualified items. The test results are as follows: the whole batch is qualified. Chemical and sanitary indexes are tested, and if the typical items are unqualified, the whole batch is unqualified. t||日 Marking, packaging, transportation, storage
日.1.1 The product should have special recycling labels on the body. 8.1.2 The product should have the following labels on the legal chain: individual labels: product weight, quantity, net weight, packaging, production, production, name & address, transportation and storage, etc. 8.2 Packaging
The packaging label should be able to ensure the safety of the product during transportation in the enterprise 8.3 During transportation, the products shall be clean, disinfected, and prevented from being pressed and placed properly. 8.4 Products shall be stored in a dry, clean, and dry place without any chemicals or harmful substances. The products shall be stored in a well-maintained place for 15 days to reduce the heat before transportation. The products shall not be stored for more than 3 days from the date of production. KANY Ka
Appendix A
: Record of Porcelain Properties
Table of Water in Air Nanliang Table
C P9B8T
t: uux 21
G44x41
0. 998 45
i. yu gri
.yuh *s
QB/T2665-2004
wg·ml:
0. 995 77
0. 995 51
0. 995 25
0. 9-13 39
u. 99.: 05
0. 992 71
0. 992.35
0. 991 63
099387
QR:T 2665-2004
/()
0. 980 21
6. 979 13
( 76 33 | | tt | 82
699967
1 95547
Tip: This standard content only shows part of the intercepted content of the complete standard. If you need the complete standard, please go to the top to download the complete standard document for free.