drafter:Jiang Caixing, Wei Mingji, Wang Xingdong, Wang Guomei, Guan Tonglin, Yu Guofang
Drafting unit:Ningbo Dongsheng Packaging Materials Co., Ltd., Shenzhen Yonghe Technology Chemical Co., Ltd., National Packaging Product Quality Supervision and Inspection Center (Jinan), China Packaging Federation
Focal point unit:National Packaging Standardization Technical Committee
This standard replaces GB/T 16719-1996 "Biaxially oriented polystyrene (BOPS) sheets". This standard specifies the product specifications, technical requirements, test methods, inspection rules, marking, packaging, transportation and storage of biaxially oriented polystyrene sheets. This standard is applicable to sheets made of polystyrene resin as the main raw material, extruded by the flat film method and biaxially oriented. Compared with GB/T 16719-1996, the main changes in this standard are as follows: - "Product classification" is changed to "Product specification", and the thickness range is adjusted to 0.100mm~0.700mm; - Added terms and definitions; - Adjusted the width deviation to 0mm~+2mm; - Cancelled the product classification; - Added the "anti-fogging" item in 5.3 "Physical and mechanical properties" in Chapter 5 of the standard; - Added 7.1 "Batching and sampling" in Chapter 7 of the standard; - Deleted "Appendix A". GB/T 16719-2008 Biaxially oriented polystyrene (BOPS) sheet GB/T16719-2008 standard download decompression password: www.bzxz.net
This standard specifies the product specifications, technical requirements, test methods, inspection rules, marking, packaging, transportation and storage of biaxially oriented polystyrene (BOPS) sheets.
This standard is applicable to sheets made of polystyrene resin as the main raw material, extruded by flat film method and biaxially oriented. || tt|| This standard replaces GB/T16719-1996 "Biaxially oriented polystyrene (BOPS) sheets".
Compared with GB/T16719-1996, the main changes of this standard are as follows:
---Change product classification to product specification, and adjust the thickness range to 0.100mm~0.700mm;
---Add terms and definitions;
---Adjust the width deviation to 0mm~+2mm;
---Cancel the product classification;
---Add the anti-fogging item in 5.3 physical and mechanical properties in Chapter 5 of the standard;
---Add 7.1 batching and sampling in Chapter 7 of the standard;
---Delete Appendix A.
This standard is proposed and managed by the National Technical Committee for Packaging Standardization.
Drafting units of this standard: Ningbo Dongsheng Packaging Materials Co., Ltd., Shenzhen Yonghe Technology Chemical Co., Ltd., National Packaging Product Quality Supervision and Inspection Center (Jinan), China Packaging Federation.
The main drafters of this standard are: Jiang Caixing, Wei Mingji, Wang Xingdong, Wang Guomei, Guan Tonglin, Yu Guofang.
The previous versions of the standards replaced by this standard are:
---GB/T16719-1996. The clauses in the following documents become the clauses of this standard through reference in this standard. For all dated referenced documents, all subsequent amendments (excluding errata) or revisions are not applicable to this standard. However, the parties who reach an agreement based on this standard are encouraged to study whether the latest versions of these documents can be used. For all undated referenced documents, the latest versions are applicable to this standard.
GB/T1040.3 Determination of tensile properties of plastics Part 3: Test conditions for film and sheet (GB/T1040.3-2006, ISO527-3:1995, IDT)
GB/T2410 Test method for light transmittance and haze of transparent plastics
GB/T2828.1 Sampling inspection procedure by attributes Part 1: Sampling plan for batch inspection based on acceptance quality limit (AQL) (GB/T2828.1-2003, ISO2859-1:1999, IDT)
GB/T2918 Standard environment for conditioning and testing of plastic specimens (GB/T2918-1998, idtISO291:1977)
GB/T5009.60 Analytical method for hygienic standard of polyethylene, polystyrene and polypropylene molded products for food packaging
GB/T6672 Determination of thickness of plastic film and sheet - Mechanical measurement method (GB/T6672-2001, idtISO4593:1993)
GB/T6673 Determination of length and width of plastic film and sheet (GB/T6673-2001, idtISO4592:1992)
GB9689 Hygienic standard of polystyrene molded products for food packaging
GB/T14216 Wetting tension test method for plastic film and sheet (GB/T14216-1993, eqvISO8296:1987)
Some standard content:
ICS55.040 National Standard of the People's Republic of China GB/16719-2008 Supervised by GB/T16719—1996 Biaxially oriented polystyrene (BOPS) sheet2008-07-18 Issued General Administration of Quality Supervision, Inspection and Quarantine of the People's Republic of China Standardization Administration of China 2009-01-01 Implementation This standard replaces GB/T16710 196 Biaxially oriented polystyrene (BOPS) sheet. Compared with CGB/T16719—1995, this standard has the following major changes: G8/T 16719—2008 Change "product classification" to "product specification", adjust the thickness range to 0.100mm~0.700mm; add terms and definitions; -Adjust the width deviation to ~+ -Cancel the product classification: Add the "anti-dew property" item in 5.3 "physical and mechanical properties" in Chapter 5 of the standard; add .1 "batch and single sample" in the standard; delete "Appendix A", This standard was proposed and approved by the National Packaging Standardization Technical Committee. The drafting units of this standard are: Ningbo Dongsheng Packaging Materials Co., Ltd., Shenzhen Yonghe Technology Chemical Co., Ltd., National Packaging Product Quality Supervision and Inspection Center (Jinan), and China Packaging Federation. The main drafters of this standard are: Jiang Caixing, Wei Mingji, Fei Xingdong, Wei Guoguan, Guan Tongdong, and Yu Tongpang. The previous versions of the standards replaced by this standard are: GB/T 16719--1996 1 Scope Double-sided oriented polystyrene (BOPS) sheet GB/T 16719—2008 This standard specifies the product specifications, technical requirements, test methods, inspection rules, marking, packaging, transportation and storage of biaxially stretched polyvinyl chloride (130OPS) sheets (hereinafter referred to as sheets). The standard is applicable to biaxially stretched polyvinyl chloride (130OPS) sheets made of 130OPS resin as the main raw material and extruded by flat film method. 2 Normative references The clauses of the following documents become the clauses of this standard through reference in this standard. For any dated referenced document, all subsequent amendments (excluding errata) or revisions are not applicable to this standard. However, the parties who reach an agreement on this standard are encouraged to study whether the latest versions of these documents can be used. For any undated referenced document, its latest version shall apply to this standard. G13/T10140.3 Determination of tensile properties of materials, Part 3: Test conditions for film sheets (GJ3/TL040.32006, IS0 GB/T 291:1977) GB/T 5993.60 Method of analysis of the hygienic standard of polyolefins, polystyrene and polypropylene products for food packaging (GB/T 6672 Determination of the thickness of plastic film and sheet by mechanical measurement (G13/T 6672-2001: id1so) 459 3:1993) GB/T6673 Determination of length and width of plastic film and sheet (GB3/6673:2001, idtI54592:1992) G139689 Hygienic standard for polyimide molded products for food packaging GB/11216 Wetting tension test method for plastic film and sheet (GB/14216993.cq VISO8296.1987) 3 Terms and definitions The following terms and definitions apply to this standard. 3.1 Stripe A continuous group of small die head patterns. Distortion The unevenness of the sheet after winding caused by the accumulation of thickness deviation. 3.3 Particie Black spots, household spots, patches, spots, etc. that can be observed by the naked eye on the sheet. 4: Product specifications The serial size of the sheet is 0.100zm0.700mm, special specifications are agreed upon by the supply and demand parties, 5 requirements 5.1 Size deviation 5.1.1 Width deviation The width deviation of the sheet is 0rnm+2mm. G/T167192008 5.1.2 Thickness deviation The thickness deviation of the material shall be in accordance with the specifications in Table 1 Nominal thickness/mm 0.100~0.250 0. 231~-0. 400 0. 401-0. 70m 5.2 Appearance quality The appearance requirements of the sheet are shown in Table 2 Crack, fold, perforation Linearity, deformation pieces/(30 cm×80 pieces/30 e×30 Diameter 1mm Diameter>1mm Thickness deviation Appearance quality Particle size 0. 5 mm~1mm Particle size ≥1 mm Appearance of roll Number of joints per roll End before roll 5.3 Physical and mechanical properties Physical and mechanical properties of sheet materials are shown in Table 3. Tampering/% Not allowed Slight, does not affect use Not allowed Surface is smooth One is allowed, and the length of each section is not less than 5°C\: The number of rolls with joints in each batch exceeds 10% Smoothness is within ±5mm, and smooth over the line Not allowed Defects that affect use Table 3 Physical and mechanical properties Tensile strength (longitudinal, inter-determined)/MF Breaking elongation (longitudinal, inter-determined)/% Anti-fog/grade Light transmittance/% Shadow density/% Wetting tension (N/n) Applicable to anti-glare sheets. bApplicable to transparent sheets. CApplicable to sheets that have been treated with corona but not coated. 2 5.4 Hygiene indicators Applicable to food The sanitary index of the sheet material for product packaging shall comply with the provisions of (139689: 6 Test method 6.1 Sampling GB/T16719.-2008 Remove 2 layers of the sample roll and cut 2 sheets of 2m long, one for dimensional deviation and appearance test, the other for physical mechanical performance and hygienic performance test. Correctly mark the corona treated surface and the coating surface. During the sampling process, the sample must not be contaminated or damaged, otherwise re-sample, 6.2 Sample state adjustment and test standard environment The state adjustment and test standard environment of the sample should comply with the standard environment and positive deviation range specified in GB/T2918: the state adjustment time shall not be less than 1h, and the test shall be carried out in this environment. 6.3 Specifications and dimensions 6.3.1 The thickness test of the sheet shall be carried out in accordance with B/T6672, and the thickness deviation shall be calculated using the maximum deviation value. 6.3.2 The width test of the sheet shall be carried out in accordance with GB/T6673. 6.4 Appearance Self-test and check under natural light. Use a 10x magnifying glass to observe and measure the diameter of the anomaly and bubble! Use a steel ruler with a scale of .5 mt to measure the end surface flatness, 6.5 Tensile strength and elongation at break The test of sheet tensile strength and elongation at break is carried out in accordance with GB/T1040.3. The specimen is type 2, with a specimen width of 15mm and an elongation of 0.1mm. The optical tool can be 100m1b.5mnl, and the test speed is 50mm/min±5mm/min. 6.6 Anti-fog property Put 60ml 80° hot water into a 100ml flat beaker, seal the beaker mouth with the test sheet, leave it for 10 minutes, and observe the water vapor distribution on the sheet surface. The anti-fog property is as follows: After the test, if the surface of the sample is covered with small water droplets and is completely opaque, it is grade 1; if the surface is covered with large water droplets and is basically opaque, it is grade 2; if there are large water droplets attached to the surface, but it is quite transparent, it is grade 3; if the sample is basically transparent and has few water droplets, it is grade 1; if the sample is completely transparent and has no fogging, it is grade 5.7 Transmittance and haze The test of transmittance and haze of the sheet shall be carried out in accordance with G13/T2110. 6. 8 Wetting tension The test of wetting tension of the sheet shall be carried out in accordance with BT14216. 6. 9 Hygiene index The test of hygiene index of the sheet shall be carried out in accordance with GB/T5009.60. 7 Inspection rules 7.1 Batch and sampling 7.1.1 Batch The sheet material inspection is carried out in batches. The sheets of the same specification produced under the same process conditions are considered as a batch. Each batch shall not exceed 1001. 7.1.2 Sampling The size deviation and appearance shall be in accordance with the normal inspection secondary sampling plan specified in (F13712828.1), the inspection level is II, and the acceptance quality limit (AQL) is 6.5. The inspection shall be carried out in accordance with the provisions of Table 4. For physical and mechanical properties and positive indicators, the sheets shall be inspected from the same batch of products. GB/T 16719--2008 13--25 51--90 91--150 151~-280 281:~500 301--1 200 1201-~3200 Inspection classification Table 4 Sampling and judgment plan for specification and appearance inspection Product inspection is divided into factory inspection and type test inspection, and the samples are collected and sent out! The inspection items are all items in the requirements except for the sanitary indicators. Acceptance number A Type inspection items are all items in the requirements. Type inspection should be carried out in any of the following situations: trial production and identification of new products or test products for transfer to factory production; after formal production, if the structure, materials, and process have significant changes, , which may affect the product performance; during normal production, it is conducted once a year; when the product has been suspended for a long time, the production is resumed; when the inspection results are significantly different from the "type inspection"; when the national quality supervision agency proposes a request for type inspection. 7.3 Determination of inspection results The unit is the rejection number R The size difference and appearance of the sheet material. If any item is unqualified: the roll of product is judged to be unqualified. The qualified batch is determined according to Table 4. 7.3.2. The physical properties of the sheet material should all meet the requirements of the standard stall; if there are unqualified items, the original batch of products should be Randomly draw double samples from the products and retest the unqualified items. If the retest still fails, the batch of products shall be judged as unqualified. 7.3.3 If any of the health indicators fail to meet the standards, the batch of products shall be unqualified. 7.3.4 If the products meet the standards according to 7.3.1, 7.3.2 and 7.3.3, the batch of products shall be judged as qualified products. 8 Marking, packaging, transportation and storage 8.1 Marking GB/16719—2008 The sheet roll or the packaging shall be accompanied by a certificate of conformity. Indicate the production order on the certificate of conformity or the instruction manual. Location, address, product name, specification, weight or length, coating surface, batch number, production date. There are packaging box dimensions (length × width × height) and signs such as anti-condensation, heat protection, and oil protection. 8.2 Packaging 8.2.1 Carton packaging: The chain roll sheet is packed with plastic film as the inner packaging, and the supporting grade box is used as the outer packaging, and the packaging tape is used to seal the hole: 8.2.2 Pallet packaging: Each roll of sheet is packed with a whole material film as the inner packaging, placed upright or lying on the pallet, protected by tile board cardboard above and below, and fixed with packaging bundles. 8.2.3 Special packaging is agreed upon by the supply and demand parties. 8.3 TransportationwwW.bzxz.Net Be careful and gentle to prevent collision, sun exposure, rain and pollution. 8. 4 Storage Sheets should be stored in a clean and dry warehouse, away from heat sources, not exposed to direct light, and not stored with toxic items. From the date of production, the shelf life of anti-penetration sheet should not exceed 1 year, and the shelf life of other sheets should not exceed 2 years. 5 GB/T 16719-2008 National Standard of the People's Republic of China Biaxially oriented polystyrene (BOPS) sheet G/T 167:92008 China Standard Publishing House Changban Publishing House No. 16, Erhebei Street, Fuxingmenwai, Beijing Postal Code: 100045 Website spc. net, cn Tel: 6852391 68517548 China Standard Publishing House Naihuangdao Printing! Printed and distributed by Xinhua Bookstores all over the country Size 880×12301/15 Word count 10,000 words First edition in October 2008 First printing in October 2008 + No.: 155069 ·1-33882 If there is any printing error, the publishing center of this publishing house will replace it. Copyright infringement will be investigated Report life phone: (010) 68533533 8002-612914 Storage The sheets should be stored in a clean, dry warehouse, away from heat sources, not exposed to direct sunlight, and not stored together with toxic substances. From the time of production, the shelf life of anti-penetration sheets should not exceed 1 year, and the shelf life of other sheets should not exceed 2 years. 5 GB/T 16719-2008 People's Republic of China National Standard Promotion Biaxially oriented polystyrene (BOPS) sheet G/T 167:92008 China Standard Publishing House Changban Issued No. 16, Erhebei Street, Fuxingmenwai, Beijing Postal Code: 100045 Website spc. net, cn Tel: 6852391 68517548 China Standard Publishing House Naihuangdao Printing! Printed and distributed by Xinhua Bookstores all over the country Size 880×12301/15 Word count 10,000 words First edition in October 2008 First printing in October 2008 + No.: 155069 ·1-33882 If there is any printing error, the publishing center of this publishing house will replace it. Copyright infringement will be investigated Report life phone: (010) 68533533 8002-612914 Storage The sheets should be stored in a clean, dry warehouse, away from heat sources, not exposed to direct sunlight, and not stored together with toxic substances. From the time of production, the shelf life of anti-penetration sheets should not exceed 1 year, and the shelf life of other sheets should not exceed 2 years. 5 GB/T 16719-2008 People's Republic of China National Standard Promotion Biaxially oriented polystyrene (BOPS) sheet G/T 167:92008 China Standard Publishing House Changban Issued No. 16, Erhebei Street, Fuxingmenwai, Beijing Postal Code: 100045 Website spc. net, cn Tel: 6852391 68517548 China Standard Publishing House Naihuangdao Printing! Printed and distributed by Xinhua Bookstores all over the country Size 880×12301/15 Word count 10,000 words First edition in October 2008 First printing in October 2008 + No.: 155069 ·1-33882 If there is any printing error, the publishing center of this publishing house will replace it. Copyright infringement will be investigated Report life phone: (010) 68533533 8002-61291 Tip: This standard content only shows part of the intercepted content of the complete standard. If you need the complete standard, please go to the top to download the complete standard document for free.