This standard applies to letterpress rotary inks. Letterpress rotary inks are made of pigments, mineral oils, vegetable oils, and resins, which are mixed and ground. They are used for letterpress rotary printing presses to print newspapers, books, and periodicals. QB/T 3596-1999 Lead printing rotary inks QB/T3596-1999 Standard download decompression password: www.bzxz.net
This standard applies to letterpress rotary inks. Letterpress rotary inks are made of pigments, mineral oils, vegetable oils, and resins, which are mixed and ground. They are used for letterpress rotary printing presses to print newspapers, books, and periodicals.
Some standard content:
Classification number: A17 Light Industry Industry Standard of the People's Republic of China QB/T 3596—1999 Replaces ZBA17003-1986 Lead-printed Rotary Ink Published on April 21, 1999 State Bureau of Light Industry Implementation on April 21, 1999 QR/T3596-1999 This standard is the original professional standard 78A17003-1986 Lead-printed Rotary Ink 3, which was converted into standard number QBT3596—1999 after being promulgated by the State Light Industry Administration [1999] No. 112. The content remains unchanged. This standard is proposed by the State Light Industry Administration Bureau. This standard is under the jurisdiction of the National Petroleum and Chemical Technology Bureau. This standard is regulated by Taiyuan Oil Plant and Daohua Oil Plant. The main drafter of this standard: Guo Jianzhong. This standard is implemented from the beginning, and replaces the original light industry professional standard ZBA7003-1986 printed linoleum oil issued by the Ministry of Light Industry, the light industry industry standard of the People's Republic of China Lead type rotary ink QB/T35961999 Replaces ZBA17000-19B6 This standard is applicable to letterpress rotary ink, which is made of materials, mineral oil, petroleum oil, and resin, which are mixed and ground for use in rotary printing presses to print newspapers, books and periodicals. 1 Product classification 1.1 Printing presses: The use of different sheets and printed materials is divided into five colors listed in Table 1, Table 1 135 801 135803 T#4802 2 Technical requirements The products of this standard must meet the technical indicators specified in Table 2. Table 2 Product name T&SAG2 T35803 T34801 T34802 White version high-speed rotary hot garden Nei liquid medium-speed material axis needs to be obvious Convex quality low-quality construction light rotation quantity is close but standard Edition book wheel special black 3 Over-shame method Coloring power, 5||tt| |Product Name High-quality printing plate Relief printing plate Relief printing plate Relief printing plate Quality Index Mobility.T.rT 500~13DU 16002600 3.1 Smoke color shall be in accordance with the provisions of QB557-1983 oil-based color test method. 3.2 Fineness shall be in accordance with the provisions of QB558-1983 contact color fading strength test method. 3.3 Fineness shall be in accordance with the provisions of QB559-1983 oil fineness test method. Approved by the State Bureau of Light Industry on 1999-D4-21 Fluidity, mm Implemented on 1999-04-21 QB/T35961999 3.4 Viscosity shall be in accordance with the provisions of QB574-1934 Oil Viscosity Test Method. 3.6 Viscosity shall be in accordance with the provisions of QB564-1963 Oil Viscosity Test Method. 3.6 Fluidity shall be in accordance with the provisions of QB5601983 Oil Viscosity Test Method. 3.7 Oil fluidity test method 3.7.1 Principle of oil fluidity test A fixed oily product is placed on a vertical film plate and the sag length of the oil within 2min is observed. The result is expressed in mm/2min. 3-7.27 Tools and materialswwW.bzxz.Net a. 250mm long, 80mm wide, and 1mm thick block b. A glass stand with a pipette, a small ink knife, a timer, and a timer. 3.7.3 Test monitoring steps 3.7.3.1 The oil column, glass plate, and pipette should reach the test temperature. 3.1.3.2 Wipe the test glass with cotton wool. The test sample should be scratched with an ink knife. 3.7.3.3 Take the sample by suction. Make sure the remaining amount is level. 3.7.3.4 Sweep the ink sample out of the pipette quickly. Place the glass on the vertical stand. At the same time, the timer should be set. The speed should be within 2m. Measure the flow at both ends. The length is the flow rate of the oil. 3.7.3. 5 The above tests are conducted in the following rooms: 2) C system, the rate of measurement is changed, and the total amount is taken. 3.7.4 Notes 3.7.4.1 Strictly control the test temperature. 3.7.4.2 Use the molten metal to remove the glass plate. 3.7.4.3 When using the ink-absorbing tube to take samples, no bubbles should be introduced. Test rules 4.1 Before the product leaves the factory, the production and inspection department is responsible for the inspection. If it meets the technical indicators, each product should be accompanied by the model, product name, batch number, net weight, and production date. 42 The receiving unit shall register the receipt. According to the technical indicators listed in this standard, the internal inspection personnel shall conduct all or part of the inspections. According to the batch size, the sampling rate is 5% 19 times, and the sampling volume is not less than 2g per cycle. 4.3 When sampling, the dust and debris on the oil should be removed to prevent foreign debris from entering the oil sample. 4.4 During the acceptance, if it is found that the technical indicators are not met, a new sampling should be conducted. If the result still does not meet the requirements of this standard, the manufacturer and the acceptance unit shall jointly negotiate and solve it. 5 Marking, packaging, transportation, storage 5.1, 7-plate rotary oil is packaged in two kinds of quick-catch packaging. 5.1.1 High, medium and low speed rotary oil of relief printing is packaged in 100kg iron barrels. 5.1.2 Plate rotary oil is packaged in 15kg iron barrels. 5.2 The outer surface of the packaging iron barrel should be sprayed with the trademark, manufacturer's name, product name, model, quantity, batch number, production date and the mark "Do not reverse capital". 5.3 The product shall not be stored for days and shall not be close to fire sources. 5.4 During transportation and handling, it shall not be placed, hardened or damaged to prevent deformation of the iron. 2 QB/T3596-1999 This product can be transported by various transportation methods such as vehicles, ships and airplanes. 5. 5 5 This product is stored according to the conditions in 5.3. The effective storage period is: years from the date of production. 5.6 5.7 During the effective storage period, individual technical labels of this product are allowed to change, but the manufacturer guarantees that it will be used. 3 Tip: This standard content only shows part of the intercepted content of the complete standard. If you need the complete standard, please go to the top to download the complete standard document for free.