This standard applies to synthetic scheelite (also known as calcium tungstate) obtained by smelting, which is used in the production of ammonium paratungstate, tungsten trioxide, ferrotungsten, alloy steel, hard alloy, tungsten material, tungsten wire and tungsten alloy. GB/T 5192-1985 Technical conditions for synthetic scheelite GB/T5192-1985 standard download decompression password: www.bzxz.net
Some standard content:
National Standard of the People's Republic of China GB5192—85 Technical requirements of synthetic scheelite Technical requirements of synthetic scheelite1985-0518Promulgated National Bureau of Standards Implementation on 1986-03-01 National Standard of the People's Republic of China Technical requirements of synthetic scheeliteUDC661.878 GB5192—85 This standard applies to synthetic scheelite (also known as calcium tungstate) obtained by smelting, which is used in the production of ammonium paratungstate, tungsten trioxide, ferrotungsten, alloy steel, cemented carbide, tungsten material, tungsten wire and tungsten alloy. 1 Technical requirements Synthetic scheelite is divided into three grades and six types according to chemical composition and smelting method. Calculated by dry ore grade, it should meet the requirements of the following table: % Not less than Note: Class I in the table is for pyrometallurgy, and Class II is for hydrometallurgy. Cu Quality, not more than Not more than 1.2 Synthetic scheelite products for hydrometallurgy are white powder with uniform particle size, and -200 mesh is not less than 80%. If the user has special requirements, it shall be negotiated by the supply and demand parties. 1.3 There shall be no foreign inclusions in the synthetic scheelite products. 2 Test methods and inspection rules 2.1 The chemical composition analysis of synthetic scheelite shall be carried out in accordance with YB602 (1~12)-78 "Chemical Analysis Method of Tungsten Concentrate". 2.2 The sampling and preparation of synthetic scheelite shall be carried out in accordance with GB441484 "Sampling and Preparation Methods for Packaged Tungsten Concentrate". 2.3 If the re-test results of the purchaser are inconsistent with the quality certificate, it may be submitted to the supplier within three months from the date of receipt of the product, and the supply and demand parties shall negotiate to resolve the issue. If arbitration is required, the supply and demand parties shall jointly take samples at the purchaser's side. 2.4 Arbitration sampling and analysis shall be carried out in accordance with Articles 2.2 and 2.1 of this standard respectively. 2.5 The products shall be inspected and accepted by the supplier's technical supervision department. 2.6 The same grade and type of synthetic scheelite are supplied in batches, and the weight of each batch shall not exceed 5t. 3 Packaging, marking and quality certificate 3.1 Synthetic scheelite is packaged in three layers, with the inner layer being a plastic bag, the middle layer being a latex bag, and the outer layer being a sack. The bag mouth should be sealed tightly. 3.2 The net weight of each bag is 50kg. 3.3 The product packaging bag shall be marked with: Promulgated by the National Bureau of Standards on May 18, 1985 Implemented on March 1, 1986 Supplier name or mark, Product name, grade, type, Batch number, Net weight. Each batch of products shall be accompanied by a quality certificate, indicating: Supplier name: Product name, grade, type, Batch number, Net weight, Gross weight, Physical properties and chemical composition; Number of packages: Delivery date, This standard number. Additional remarks: GB5192-85 This standard is proposed by China National Nonferrous Metals Industry Corporation. This standard was drafted by Ganzhou Select Factory. The main drafter of this standard is Zeng Yue. Ministry of Metallurgical Industry of the People's Republic of China Ministry Standard Watch Case Steel Pipe Varieties This standard applies to special-shaped seamless steel pipes for manufacturing high-alloy steel watch cases. 1 The shape, size and allowable deviation of the steel pipe shall comply with the provisions of the following figure. r0.2 R17.1-0-1 2 The length of the steel pipe is 0.1 meter to 4 meters. 3 The steel pipe should be cut at right angles. 4 The steel pipe shall not have significant torsion. 5 The chemical composition of the steel pipe shall be in accordance with the relevant standards. 6 The marking of the steel pipe shall be agreed upon by the supply and demand parties. Ministry of Metallurgical Industry of the People's Republic of ChinabZxz.net Shanghai Metallurgical Bureau YB446-64 January 1, 1966 Shanghai Metallurgical Bureau Tip: This standard content only shows part of the intercepted content of the complete standard. If you need the complete standard, please go to the top to download the complete standard document for free.